Dewatering member with a composite body for a paper or board machine and method for manufacturing a dewatering member with a composite body for a paper or board machine

ABSTRACT

A dewatering member for a paper or board machine has a composite body ( 13 ) and a hard surface layer ( 12 ). The composite body ( 13 ) is manufactured in a pultrusion process. An adhesion layer ( 11 ) is formed on desired outer surfaces of the composite body ( 13 ) such that reinforcements passed to the adhesion layer ( 11 ) have been passed to the pultrusion process through a separate resin bath, to which an adhesion improving agent has been added such that the hard surface layer ( 12 ) can be applied directly onto it, and reinforcements forming the inner portion of the composite body ( 13 ) have been passed to the pultrusion process through a second resin bath. The composite body ( 13 ) is coated with a hard coating layer ( 12 ) produced by thermal spraying, and the coating ( 12 ) is ground.

CROSS REFERENCES TO RELATED APPLICATIONS

[0001] This application claims priority on Finnish Application No. 20012261, Filed Nov. 21, 2001, the disclosure of which is incorporated by reference herein.

STATEMENT AS TO RIGHTS TO INVENTIONS MADE UNDER FEDERALLY SPONSORED RESEARCH AND DEVELOPMENT

[0002] Not applicable.

BACKGROUND OF THE INVENTION

[0003] The invention relates to a dewatering member with a composite body for a paper or board machine and to a method for manufacturing a dewatering member with a composite body for a paper or board machine.

[0004] In paper machines, among other things, different suction boxes, loading elements, etc. are used for dewatering, in which boxes and elements a foil structure is often used in which the foils, on the one hand, support or load a wire/felt and, on the other hand, doctor the water being drained from the paper web off the surface of the wire. The foils are subjected to heavy wear against the wire, and therefore the foils shall be made of a material that is especially resistant to wear.

[0005] A problem in these prior art arrangements which have used a foil made of a ceramic has also been caused by the fact that ceramic materials do not ordinarily withstand high stresses. The present applications of dewatering devices require relatively narrow foils, which are very difficult to manufacture out of ceramic. Narrow ceramic foils are also very problematic from the standpoint of the stresses caused by loading.

[0006] Foils made of ceramic have also been problematic in that ceramic pieces may have risen from the desired level, with the result that the surface level of the foil structure that guides the wire and determines its run is not even any more.

[0007] With respect to the prior art, reference is made to FI application publication 940884, which discloses a method for manufacturing a structure comprising a set of foils for a dewatering device of a paper machine, and a structure comprising a set of foils for a dewatering device of a paper machine. In this prior art arrangement, a foil in the structure of a set of foils is attached to a frame structure of a web forming and/or dewatering device or to an equivalent support piece, and the surface of the foil facing the wire has been machined to a desired level or shape, after which the surface of the foil facing the wire has been coated with a ceramic coating, which is in direct contact with the foil body.

[0008] With respect to the prior art, reference is also made to FI application publication 943777, which discloses a dewatering member for a paper machine and a method for manufacturing it. In this prior art arrangement, the dewatering member comprises a body and a ceramic wearing surface. The body comprises an elongated profile which forms a bounded space into which it has been possible to cast a flowing material. The body has also included at least one surface for attaching the wearing surface. The body comprises thermoset plastic which fills the bounded space at least partly. The wearing surface is a ceramic coating thermally sprayed onto the surface of the body profile.

[0009] Today, the dewatering foils used in paper and board machines are manufactured of piece ceramic attached to a body. Small ceramic pieces made by sintering are attached to the body either mechanically or by gluing. A problem with piece ceramic has been, among other things, the “piano-key effect” in which glued ceramic pieces rise to different levels on the surface of the foil. In that case, the pieces which have risen to a higher level produce harmful marks on the paper web that is being manufactured. One problem with the prior art dewatering members has also been that pieces have become detached or split.

SUMMARY OF THE INVENTION

[0010] An object of the invention is to provide a dewatering member in which the drawbacks of the prior art arrangements are eliminated or at least minimized.

[0011] An object of the invention is also to provide a dewatering member which is durable and economical to manufacture.

[0012] In accordance with the invention, in the manufacturing stage of the composite body of the dewatering member, reinforcements forming a surface layer in a pultrusion process are conveyed through a separate resin bath, into which a powder that improves adhesion has been added, for example, a metal powder, for example, NiCr powder, for example, over 50 wt. %, whereby an adhesion layer is produced on the composite by means of pultrusion, said adhesion layer being, for example, a surface layer which is rich in nickel-chromium and onto which thermal spraying can be directly carried out. Thus, there is no need to add any separate structure to the surface of the foil body at a later stage after the manufacturing process of the composite, for example, a wire mesh or metal wire to enable adhesion of a coating, as needed in the prior art arrangements, but, instead, in accordance with the invention, an adhesion improving agent, for example, a nickel-chromium powder is introduced into the composite already in the pultrusion stage, whereby it is very well locked into the resin fibre structure and does not cause any discontinuity in the structure, which occurs in the applications known in themselves in the prior art, in which a separate resin+filler layer is added to the body at a later stage.

[0013] In accordance with the invention, a durable structure having a high mechanical strength is achieved by modifying the fibre structure.

[0014] The dewatering members in accordance with the invention comprise a composite body coated with a hard ceramic coating. The ceramic coating is a thermally sprayed ceramic coating which has a high wear resistance and toughness. The adhesion of the hard coating to the composite body is provided by forming an adhesion layer onto the composite body in the pultrusion manufacturing stage, which adhesion layer considerably improves adhesion. In the pultrusion process, the reinforcements which will form the adhesion layer are conveyed through a separate resin bath, into which an adhesion improving agent, for example, a metal, preferably an NiCr or tungsten powder, has been added, said reinforcements being passed in pultrusion to the surface layer of the body.

[0015] In accordance with the invention, the dewatering foil with a composite body for a paper or board machine comprises a wear-resistant ceramic surface, which is made, for example, by thermal spraying, whereby a uniform ceramic surface is achieved, so that the problems of the prior art arrangements are not encountered, for example, rising of ceramic pieces to different levels, i.e. the “piano-key effect” known in the prior art, which occurs, for example, in sintered bulk ceramic foils. Cost savings are also achieved by means of the arrangement in accordance with the invention. In connection with the invention, a further benefit is also attained by the use of the pultrusion process enabling continuous manufacture, which is advantageous in respect of its costs. Moreover, ceramic manufactured by thermal spraying can be ground or re-coated, if needed, and it is easier to treat than when prior art piece ceramic is used.

[0016] In accordance with one application of the invention, the coating of the composite foil body having a filler incorporated therein takes place such that a nickel-chromium layer is first thermally sprayed onto the surface of the composite, for example, by an HVOF method, onto which layer it is further possible to spray a wear-resistant ceramic, for example, an Al₂O₃ or Cr₂O₃ or hard metal coating. The sprayed ceramic can be further ground to the required surface roughness value and, when the need arises, it can also be surface-sealed and/or surface-treated.

[0017] The invention is suitable for use in connection with different dewatering members of a paper or board machine, for example, in connection with the manufacture of a cover for a felt suction box.

[0018] In the following, the invention will be described in more detail with reference to the figures in the appended drawing, but the invention is not by any means meant to be narrowly limited to the details of them.

BRIEF DESCRIPTION OF THE DRAWINGS

[0019]FIG. 1 is a schematic view of a dewatering member of a paper or board machine.

[0020]FIG. 2 is a schematic view of a method for manufacturing a dewatering foil for a paper or board machine.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0021]FIG. 1 schematically shows a dewatering member, for example, a foil 10 of a dewatering device, comprising a composite body 13, an adhesion layer 11 and a hard coating 12.

[0022] According to the diagram of the manufacturing method shown in FIG. 2, reinforcements A of the surface layer, i.e. the adhesion layer 11 of the foil 10, of the body 13 of the dewatering member 10 shown in FIG. 1 are passed into a bath B, which is a resin bath containing a filler, and into a second resin bath C which does not contain any filler. From the resin baths B, C the structure is conducted in layers into a pultrusion die D, so that the fibre-containing material passed from the separate resin bath B will be in the pultrusion process D on the surface of the dewatering foil 10, i.e. of a finished profile F. By this means, the composite body 13 is provided with an adhesion layer 11, which composite body is finally coated with a hard coating layer 12 by thermal spraying. The resin alloy in the bath B comprises metallic, e.g. nickel-chromium particles/fillers, which are thus passed to the surfaces of the body 13 of the dewatering member and, when needed, to the edges.

[0023] In accordance with the invention, a filler-containing adhesion layer material is passed from the separate bath B to the surface area of the composite body 13 to a depth of at least one millimeter, most advantageously to a depth of 1-4 mm, thereby providing an even adhesion layer 11, for example, a nickel-chromium surface, to which the thermal spraying of the hard surface layer 12 adheres. The adhesion particle can also be of the same material as the coating itself. The fillers of the adhesion layer 11 are incorporated such that the desired outer surfaces of the wearing surface of the body 13 of the dewatering member 10 are of the desired adhesion material.

[0024] Thus, the method in accordance with the invention comprises three working steps: manufacturing a composite body with its adhesion layer, adding a coating to it by thermal spraying, and grinding the foil. 

We claim:
 1. A dewatering member with a composite body for a paper or board machine, comprising a composite body and a hard surface layer, wherein the composite body has been manufactured in a pultrusion process, and that an adhesion layer is formed on desired outer surfaces of the composite body such that reinforcements passed to the adhesion layer have been passed to the pultrusion process through a separate resin bath, to which an adhesion improving agent has been added such that the hard surface layer can be applied directly onto it, and that reinforcements forming the inner portion of the composite body have been passed to the pultrusion process through a second resin bath.
 2. The dewatering member of claim 1, wherein the reinforcements of the adhesion layer have been conveyed through a resin bath to which a metal powder has been added.
 3. The dewatering member of claim 2 wherein the metal powder comprises a nickel-chromium powder.
 4. The dewatering member of claim 1 wherein the surface layer has been formed by thermal spraying.
 5. A dewatering member for a paper or board machine, comprising a composite body manufactured in a plutrusion process, the body having an inner portion formed of reinforcements which have passed through a first resin bath, and an adhesion layer formed of second reinforcements which have passed through a second different resin bath having an adhesion improving agent added thereto; and a thermal spray coating applied hard surface layer is applied to the adhesion layer.
 6. The dewatering member of claim 5, wherein the second resin bath through which the second reinforcements have passed includes an added metal powder.
 7. The dewatering member of claim 6 wherein the metal powder comprises a nickel-chromium powder.
 8. A method for manufacturing a dewatering member for a paper or board machine, comprising the steps of: passing first reinforcements through a first resin bath to a pultrusion process; and passing second reinforcements through a second resin bath separate from the first resin bath to said pultrusion process, the second resin bath having an adhesion improving agent added thereto, wherein a composite body of the dewatering member is formed in said pultrusion process which has a surface layer comprised of said second reinforcements, and an inner portion of the body comprised of said first reinforcements.
 9. The method of claim 5, wherein the second resin bath has a metal powder added thereto.
 10. The method of claim 6 wherein the metal powder comprises a nickel-chromium powder.
 11. The method of claim 6 further comprising the step of thermal spraying a surface layer on the composite body.
 12. The method of claim 6 further comprising the steps of: thermal spraying a hard coating on the composite body; and grinding said coating. 